    Optical properties of GaTe-ZnTe nanolamellae composite [Articol]
    (2015) Spalatu, Nicolae; Evtodiev, Igor; Caraman, Iuliana; Evtodiev, Silvia; Rotaru, Irina; Caraman, Mihail; Untilă, Dumitru
    A material composed of GaTe and ZnTe crystallites with average diameter of ~ 37 nm and 68 nm respectively was obtained by heat treatment at the temperature of 1000K and 1073K of GaTe plates in Zn vapour for 24 hours. The absorbance spectra of composite material obtained at 1073K and that calculated from diffuse reflection using the Kubelka-Munk formula contains the bands characteristic for light absorption in ZnTe and GaTe crystallites. The photoluminescence spectrum of composite material at the temperature of 80K is composed to the excitonic band in GaTe and impurity bands of ZnTe crystallites.
  • Thumbnail Image
    Item
    Structura cristalină şi proprietăţile optice ale materialelor compozite obţinute prin intercalare cu Cd a monocristalelor de GaSe și GaTe [Articol]
    (CEP USM, 2019) Vatavu, Elmira; Dmitroglo, Liliana; Untilă, Dumitru; Sprincean, Veaceslav; Caraman, Mihail
    Formarea prin tratament termic a monocristalelor de GaSe şi GaTe în vapori de Cd a materialului compus din cristalite de GaSe şi CdSe şi, respectiv, de GaTe şi CdTe cu dimensiuni nanometrice a fost confirmată prin analiza diagramelor XRD, imaginilor SEM şi a difuziei combinate Raman. Nanocompozitele GaSe-CdSe şi GaTe-CdTe sunt materiale fotoluminescente (FL) în regiunea oranj-roşu a spectrului. Benzile de FL a compozitelor sunt formate prin suprapunerea benzilor de FL impuritară a cristalitelor componente ale nanocompozitelor GaSe-CdSe şi GaTe-CdTe.