2. Articole
Permanent URI for this collectionhttps://msuir.usm.md/handle/123456789/47
Browse
3 results
Search Results
Item FOTOLUMINESCENŢA STRATURILOR NANOLAMELARE DE GaSe OBŢINUTE PRIN INTERCALAREA CU Cd(2012) Dmitroglo, Liliana; Evtodiev, Igor; Caraman, Iuliana; Nedeff, Valentin; Dafinei, AdrianS-au analizat spectrele de emisie fotoluminescentă a lamelor monocristaline p-GaSe cu concentraţia golurilor3•1014 cm-3 şi a lamelor intercalate cu Cd în fază de vapori la temperatura 500 °C. Durata tratamentului termic a fost de 20 şi 24 ore. Spectrul de emisie al cristalelor de GaSe conţine liniile excitonilor direcţi localizaţi cu energia de legătură ~6 meV, prima repetare fononică a acestora (ħωf =20 meV) şi banda de emisie a excitonilor indirecţi cu emisia fononilor cu energia 15 meV. Spectrul de emisie a compozitelor obţinute prin intercalarea lamelor de GaSe cu Cd se obţine în rezultatul suprapunerii benzilor de emisie a compusului CdSe şi banda impuritară a monoseleniurii de galiu. Structura spectrului FL depinde de durata tratamentului termic. La majorarea timpului de tratament se amplifică subbanda corespunzătoare compusului CdSe.Item NANOLAMELLAR STRUCTURES OF OXIDE-AIIIBVI:Cd SEMICONDUCTORS TYPE FOR USE AS DETECTORS OF RADIATION IN THE UV SPECTRAL REGION(Technical University of Moldova, 2011-07-07) Dmitroglo, Liliana; Untila, Dumitru; Chetruș, Petru; Evtodiev, Igor; Caraman, Iuliana; Lazăr, Gabriel; Nedeff, ValentinIn the paper, optical and photoelectrical properties of GaSe and InSe single crystal films of 10-5÷10-7 m submicron thickness and of semiconductor-native oxide structures obtained by annealing at (450÷700)°C in a normal atmosphere, are studied. The absorption spectrum of InSe lamella as well as of GaSe lamella in the energetic range from the red threshold up to 4,5 eV contains three bands with a rapid increase of the absorption coefficient which varies in the limits of (100÷106) cm-1 At the energies higher than 1,25 eV and 2,01 eV for InSe and GaSe respectively the light absorption are determined by the direct optical transitions in the centre of the Brillouin zone and at the energies higher than. At the absorption coefficients of (100÷102)cm-1 the indirect optic transitions are present. 3,0 eV also by the direct optical transitions in the points of the bands high symmetry. The resistive photosensitivity bands cover the spectral range Eg≤ hν ≤ 4,5 eV for lamellar photoresistors in which electric field EC6. The resistive photosensitivity band width could be controlled by the lamella thickness for d ≥1μm. The open circuit voltage spectral distribution is analysed from which results that at the oxidation temperature of 700°C in GaSe layer at the heterojunction interface the defects are formed on which the charge carriers, collected in the junction, are dissipated. The noneequilibrium charge carrier free path is of 0,8 μm.Item GROWTH AND CHARACTERIZATION OF Eu DOPED GaSe SINGLE CRYSTALS BY X-RAY DIFFRACTION AND RAMAN SPECTROSCOPY(CEP USM, 2017) Untila, Dumitru; Evtodiev, Igor; Caraman, Iuliana; Kantser, Valeriu; Spalatu, Nicolae; Dmitroglo, Liliana; Evtodiev, Silvia; Spoială, Dorin; Rotaru, Irina; Gașin, PetruGaSe single crystals doped with Eu (0.025, 0.05, 0.5, 1.0 and 3.0 at%) were grown by Bridgman method using Ga, Se and Eu elementary components. The crystalline structure and vibration modes of the GaSe: Eu crystals lattice were studied by X-ray diffraction and Raman spectroscopy. Eu atoms arranged in the van der Waals space of GaSe: Eu crystals form Eu-Se valence bonds and restructure hexagonal lattice of GaSe leading to EuGa2Se4 crystallites formation. Defects generated by EuGa2Se4 crystallites lead to broadening and shifting of single phonon peaks present in Raman spectra towards shorter wavenumbers, and at the same time, activate the longitudinal optical vibrations of EuSe sublattice.